prikaz prve stranice dokumenta Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons
No public access
Other - Other
Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons
In: Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations. Bugarska: Scientific-technical union of mehanical engineering Bulgaria, 2019. pp. 63-65. urn:nbn:hr:115:676311
Severinski, Ante; Glavaš, Zoran; Štrkalj, Anita

Institutional repository: Repository of Faculty of Metallurgy University of Zagreb

Cite this document

Severinski, A., Glavaš, Z. & Štrkalj, A. (2019). Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons. Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations (pp. 63-65). Bugarska: Scientific-technical union of mehanical engineering Bulgaria. Retrieved from https://urn.nsk.hr/urn:nbn:hr:115:676311

Severinski, Ante, et al. "Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons." Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations, Scientific-technical union of mehanical engineering Bulgaria, 2019, pp. 63-65. https://urn.nsk.hr/urn:nbn:hr:115:676311

Severinski, Ante, Zoran Glavaš and Anita Štrkalj. "Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons." In Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations, 63-65. Bugarska: Scientific-technical union of mehanical engineering Bulgaria, 2019. Accessed 2024 July 07. https://urn.nsk.hr/urn:nbn:hr:115:676311

Severinski, A., Glavaš, Z. and Štrkalj, A. (2019) 'Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons', Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations, Scientific-technical union of mehanical engineering Bulgaria, Bugarska, pp. 63-65. Available at: https://urn.nsk.hr/urn:nbn:hr:115:676311 (Accessed 07 July 2024)

Severinski A, Glavaš Z, Štrkalj A. Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons. Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations. Bugarska: Scientific-technical union of mehanical engineering Bulgaria; 2019. Pp. 63-65. [cited 2024 July 07] Available at: https://urn.nsk.hr/urn:nbn:hr:115:676311

A. Severinski, Z. Glavaš and A. Štrkalj, "Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons", Proceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations Bugarska: Scientific-technical union of mehanical engineering Bulgaria, 2019. [Online] Available at: https://urn.nsk.hr/urn:nbn:hr:115:676311 [Accessed: 07 July 2024]

Metadata
Title (english)Effect of cooling rate and silicon content on graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons
AuthorAnte Severinski
AuthorZoran Glavaš
MBZ: 262725
AuthorAnita Štrkalj
MBZ: 289540
Author's institutionUniversity of Zagreb
Faculty of Metallurgy
Scientific / art field,
discipline and subdiscipline		TECHNICAL SCIENCES
Metallurgy
Abstract (english)
Effect of the cooling rate (section thickness) on the graphite morphology and austenite transformation in solid solution strengthened ferritic ductile cast irons was analysed in this paper. Three melts with the following silicon contents were made: 3.11, 3.8 and 4.22 wt.%. The analysis was carried out on test castings containing seven different section thicknesses: 3, 12, 25, 38, 50, 75, and 100 mm. Obtained results show that the nodule count and nodularity decrease with increasing section thickness (i.e. with a decrease in the cooling rate). The increase in silicon content from 3.11 to 4.22 wt.% resulted in an increase in nodule count and nodularity in section thicknesses of 3, 12, 25 and 38 mm. However, in thick sections, i.e. in section thicknesses of 50, 75 and 100 mm, the increase in silicon content resulted in a decrease in nodule count and nodularity. In these sections, the number of very small irregular graphite particles and clusters of graphite particles that look like chunky graphite increased with the increase in silicon content. In test castings containing 3.8 and 4.22 wt.% Si the amount of ferrite in the metal matrix increases with increasing section thickness. Fully ferritic metal matrix is obtained in section thicknesses of 25, 38, 50, 75 and 100 mm. All sections of the test casting containing 3.11 wt.% Si have a certain proportion of pearlite.
Keywords (english)
Languageenglish
Publication typeOther - Other
Publication statusPublished
Peer reviewPeer review - international
Publication versionPublished version
Publication titleProceedings book of the Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations
Numberingpp. 63-65
p-ISSN2535-0218
e-ISSN2535-0226
URN:NBNurn:nbn:hr:115:676311
Publication2019
ConferenceTitle: Vth International Scientific Conference - Material Science- Nonequilibrium Phase Transformations
Location: Varna, Bulgaria
Start date: 2019-09-09
End date: 2019-09-12
Assembly type: Lecture
Document URLhttp://bib.irb.hr/1022747
Type of resourceText
PublisherScientific-technical union of mehanical engineering Bulgaria
Publishing placeBugarska
Access conditionsClosed access
Terms of useLicence In copyright icon
Created on2019-10-03 09:37:36