prikaz prve stranice dokumenta Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium
  Download
PDF 2.7 MB
Scientific paper - Original scientific paper
Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium
Engineering Power : Bulletin of the Croatian Academy of Engineering, 17 (2022), 3; 19-27. urn:nbn:hr:115:096503
Begić Hadžipašić, Anita; Brajčinović, Sandra; Rajković, Marija

Institutional repository: Repository of Faculty of Metallurgy University of Zagreb

Cite this document

Begić Hadžipašić, A., Brajčinović, S. & Rajković, M. (2022). Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium. Engineering Power : Bulletin of the Croatian Academy of Engineering, 17. (3), 19-27. Retrieved from https://urn.nsk.hr/urn:nbn:hr:115:096503

Begić Hadžipašić, Anita, et al. "Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium." Engineering Power : Bulletin of the Croatian Academy of Engineering, vol. 17, no. 3, 2022, pp. 19-27. https://urn.nsk.hr/urn:nbn:hr:115:096503

Begić Hadžipašić, Anita, Sandra Brajčinović and Marija Rajković. "Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium." Engineering Power : Bulletin of the Croatian Academy of Engineering 17, no. 3 (2022): 19-27. https://urn.nsk.hr/urn:nbn:hr:115:096503

Begić Hadžipašić, A., Brajčinović, S. and Rajković, M. (2022) 'Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium', Engineering Power : Bulletin of the Croatian Academy of Engineering, 17(3), pp. 19-27. Available at: https://urn.nsk.hr/urn:nbn:hr:115:096503 (Accessed 26 December 2024)

Begić Hadžipašić A, Brajčinović S, Rajković M. Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium. Engineering Power : Bulletin of the Croatian Academy of Engineering [Internet]. 2022 [cited 2024 December 26];17(3):19-27. Available at: https://urn.nsk.hr/urn:nbn:hr:115:096503

A. Begić Hadžipašić, S. Brajčinović and M. Rajković, "Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium", Engineering Power : Bulletin of the Croatian Academy of Engineering, vol. 17, no. 3, pp. 19-27, 2022. [Online]. Available at: https://urn.nsk.hr/urn:nbn:hr:115:096503. [Accessed: 26 December 2024]

Metadata
Title (english)Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium
AuthorAnita Begić Hadžipašić
AuthorSandra Brajčinović
AuthorMarija Rajković
Author's institutionUniversity of Zagreb
Faculty of Metallurgy
Scientific / art field,
discipline and subdiscipline		TECHNICAL SCIENCES
Metallurgy
Abstract (english)
In this research, electrochemical and metallographic tests were carried out on tool steel for cold and hot work, as well as steel for cementation, with the goal to obtain corrosion parameters to determine which of the examined samples is more resistant to local pitting corrosion. Electrochemical tests were performed in a medium of 3.5% NaCl, and were based on conducting cyclic anodic polarization in the potential range from -2000 mV to 200 mV vs SCE and vice versa. The results of the research showed that all three samples are subject to pitting corrosion, but the worst was the cementing tool steel sample X19NiCrMo4, which had the lowest pitting potential. The W600 tool steel sample for hot work proved to be the best, with the highest pitting potential. The results of the electrochemical tests coincide with the metallographic tests, because after corrosion in the chloride medium only the beginnings of pitting corrosion are visible on the surface of the W600 sample in the form of partial accumulations of corrosion products, while the X19NiCrMo4 cementing steel sample was completely covered with corrosion products, which means that of the three tested tool steels, cementing steel is the most susceptible to pitting corrosion and is not recommended for use in conditions where it comes into contact with chloride ions. The martensitic microstructure of cementing tool steel is responsible for the very low pitting potential and, consequently, pronounced pitting corrosion. On the other hand, the W600 tool steel showed better corrosion resistance due to its finer grain and uniform carbide distribution.
Keywords (english)
Languageenglish
Publication typeScientific paper - Original scientific paper
Publication statusPublished
Peer reviewPeer review - domestic
Publication versionPublished version
Journal titleEngineering Power : Bulletin of the Croatian Academy of Engineering
Numberingvol. 17, no. 3, pp. 19-27
p-ISSN1331-7210
URN:NBNurn:nbn:hr:115:096503
Publication2022
ProjectNumber: KK.01.1.1.02.0020
Title (croatian): Centar za ljevarstvo - SIMET
Title (english): Center for casting - SIMET
Acronym: SIMET
Leader: Zdenka Zovko Brodarac
Jurisdiction: Croatia
Funding stream: European Regional Development Fund
ProjectNumber: KK.01.1.1.02.0022
Title (croatian): Virtulab – Integrirani laboratorij za primarne i sekundarne sirovine
Acronym: Virtulab
Leader: Sibila Borojević Šoštarić
Jurisdiction: Croatia
Funding stream: European Regional Development Fund
Document URLhttps://hrcak.srce.hr/clanak/435996
Type of resourceText
Access conditionsOpen access
Terms of useLicence In copyright icon
Created on2024-04-29 10:59:51