Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing
Materiali in tehnologije, 48 (2014), 5; 713-718. urn:nbn:hr:115:226928
Ivanić, Ivana; Gojić, Mirko; Kožuh, Stjepan; Kosec, Borut

Institutional repository: Repository of Faculty of Metallurgy University of Zagreb

Cite this document

Ivanić, I., Gojić, M., Kožuh, S. & Kosec, B. (2014). Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing. Materiali in tehnologije, 48. (5), 713-718. Retrieved from https://urn.nsk.hr/urn:nbn:hr:115:226928

Ivanić, Ivana, et al. "Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing." Materiali in tehnologije, vol. 48, no. 5, 2014, pp. 713-718. https://urn.nsk.hr/urn:nbn:hr:115:226928

Ivanić, Ivana, Mirko Gojić, Stjepan Kožuh and Borut Kosec. "Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing." Materiali in tehnologije 48, no. 5 (2014): 713-718. https://urn.nsk.hr/urn:nbn:hr:115:226928

Ivanić, I., et al. (2014) 'Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing', Materiali in tehnologije, 48(5), pp. 713-718. Available at: https://urn.nsk.hr/urn:nbn:hr:115:226928 (Accessed 23 November 2024)

Ivanić I, Gojić M, Kožuh S, Kosec B. Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing. Materiali in tehnologije [Internet]. 2014 [cited 2024 November 23];48(5):713-718. Available at: https://urn.nsk.hr/urn:nbn:hr:115:226928

I. Ivanić, M. Gojić, S. Kožuh and B. Kosec, "Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing", Materiali in tehnologije, vol. 48, no. 5, pp. 713-718, 2014. [Online]. Available at: https://urn.nsk.hr/urn:nbn:hr:115:226928. [Accessed: 23 November 2024]

Metadata
Title (english)Microstructural analysis of CuAlNiMn shape-memory alloy before and after the tensile testing
Title (slovene)ANALIZA MIKROSTRUKTURE ZLITINE CuAlNiMn Z OBLIKOVNIM SPOMINOM PRED NATEZNIM PREIZKUSOM IN PO NJEM
AuthorIvana Ivanić
AuthorMirko Gojić
AuthorStjepan Kožuh
AuthorBorut Kosec
Author's institutionUniversity of Zagreb
Faculty of Metallurgy
Scientific / art field,
discipline and subdiscipline		TECHNICAL SCIENCES
Metallurgy
Abstract (english)
In this paper the results of a microstructural analysis before and after fracture along with the mechanical properties and hardness of the CuAlNiMn shape-memory alloy are presented. The melting of the alloy was carried out in a vacuum-induction furnace in a protective atmosphere of argon. The alloy was cast into an ingot of 15 kg. After casting the alloy was forged and rolled into rods with a diameter of approximately 10 mm. A microstructural characterization was performed with light microscopy (LM) and scanning electron microscopy (SEM) equipped with energy-dispersive spectrometry (EDS). Martensitic microstructure was observed in the rods after the deformation. The fractographic analysis of the samples after the tensile testing revealed some areas with intergranular fracture. However, the greater part of the fracture surface indicated the pattern of transgranular brittle fracture. The results of the tensile tests showed the tensile strength of 401.39 MPa and elongation of 1.64 %. The hardness of the CuAlNiMn alloy is 290.7 HV0.5.
Abstract (slovene)
V prispevku so predstavljeni rezultati analize mikrostrukture pred prelomom in po njem skupaj z mehanskimi lastnostmi in trdoto zlitine CuAlNiMn z oblikovnim spominom. Taljenje zlitine je bilo izvedeno v vakuumski pe~i v za{~itni atmosferi argona. Zlitina je bila ulita v ingot mase 15 kg. Po litju je bila zlitina kovana in zvaljana na premer pribli`no 10 mm. Karakterizacija mikrostrukture je bila izvedena s svetlobno mikroskopijo (SM) in vrsti~no elektronsko mikroskopijo (SEM), opremljeno z energijskim disperzijskim spektrometrom (EDS). Analizirana je bila martenzitna mikrostruktura zlitine CuAlNiMn pred izvedenim nateznim preizkusom. Izvedena sta bila natezni preizkus in meritve trdot. Fraktografska analiza je pokazala ve~ podro~ij z interkristalnim in pogosto transkristalnim krhkim prelomom. Rezultati nateznega preizkusa so pokazali, da je natezna trdnost 401,39 MPa in raztezek 1,64 %. Trdota zlitine CuAlNiMn je 290,7 HV0,5.
Keywords (english)
Keywords (slovene)
Languageenglish
Languageslovene
Publication typeScientific paper - Original scientific paper
Publication statusPublished
Peer reviewPeer review
Publication versionPublished version
Journal titleMateriali in tehnologije
Numberingvol. 48, no. 5, pp. 713-718
p-ISSN1580-2949
e-ISSN1580-3414
URN:NBNurn:nbn:hr:115:226928
Publication2014
Document URLhttp://mit.imt.si/Revija/izvodi/mit145/ivanic.pdf
Type of resourceText
Access conditionsOpen access
Terms of useLicence In copyright icon
Created on2017-03-09 10:02:47