diplomski rad
Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama
Zagreb: Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, 2019. urn:nbn:hr:235:396214
Novak, Josip
Sveučilište u Zagrebu
Fakultet strojarstva i brodogradnje

Institucijski repozitorij: Repozitorij Fakulteta strojarstva i brodogradnje Sveučilišta u Zagrebu

Citirajte ovaj rad

Novak, J. (2019). Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama (Diplomski rad). Zagreb: Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:235:396214

Novak, Josip. "Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama." Diplomski rad, Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, 2019. https://urn.nsk.hr/urn:nbn:hr:235:396214

Novak, Josip. "Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama." Diplomski rad, Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, 2019. https://urn.nsk.hr/urn:nbn:hr:235:396214

Novak, J. (2019). 'Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama', Diplomski rad, Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, citirano: 31.05.2024., https://urn.nsk.hr/urn:nbn:hr:235:396214

Novak J. Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama [Diplomski rad]. Zagreb: Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje; 2019 [pristupljeno 31.05.2024.] Dostupno na: https://urn.nsk.hr/urn:nbn:hr:235:396214

J. Novak, "Ocjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama", Diplomski rad, Sveučilište u Zagrebu, Fakultet strojarstva i brodogradnje, Zagreb, 2019. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:235:396214

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:235:396214
Podaci o radu
NaslovOcjena zaštitnih svojstava organiskih prevlaka na različitim metalnim podlogama
Naslov (engleski)Evaluation of corrosion protection properties of organic coatings on different metal substrates
AutorJosip Novak
MentorVesna Alar (mentor)
Ustanova koja je dodijelila
akademski / stručni stupanj		Sveučilište u Zagrebu
Fakultet strojarstva i brodogradnje
Zagreb
Datum i država obrane2019-01-24, Hrvatska
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Strojarstvo
Proizvodno strojarstvo
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Strojarstvo
Opće strojarstvo (konstrukcije)
Sažetak
The aim of this masters thesis “Evaluation of corrosion protection properties of organic coatings on different metal substrates” is to examine the corrosion resistance properties of various CED and powder coatings, commonly utilized in the automotive industry. For this purpose, standardized steel, hot-dip galvanized steel and aluminium specimens are coated and subsequently tested in accelerated corrosion tests, the emphasis being on the climatic test according to VDA 233-102. The protective properties of the coatings are additionally studied using DC and AC electrochemical methods. The main evaluation criteria are degree of rusting on surface and edges, degree of corrosion and delamination around a scribe, degree of blistering, cross cut test and Daimler scratch test. The utilized accelerated corrosion tests exhibit apparent differences in the onset and character of corrosion regarding those evaluation criteria. Key influencing factors for corrosion resistance, like coating thickness and pre-treatment methods are determined.
Sažetak (engleski)
The aim of this masters thesis “Evaluation of corrosion protection properties of organic coatings on different metal substrates” is to examine the corrosion resistance properties of various CED and powder coatings, commonly utilized in the automotive industry. For this purpose, standardized steel, hot-dip galvanized steel and aluminium specimens are coated and subsequently tested in accelerated corrosion tests, the emphasis being on the climatic test according to VDA 233-102. The protective properties of the coatings are additionally studied using DC and AC electrochemical methods. The main evaluation criteria are degree of rusting on surface and edges, degree of corrosion and delamination around a scribe, degree of blistering, cross cut test and Daimler scratch test. The utilized accelerated corrosion tests exhibit apparent differences in the onset and character of corrosion regarding those evaluation criteria. Key influencing factors for corrosion resistance, like coating thickness and pre-treatment methods are determined.
Ključne riječi
Ključne riječi (engleski)
Jezikhrvatski
URN:NBNurn:nbn:hr:235:396214
Studijski programNaziv: Strojarstvo
Vrsta studija: sveučilišni
Stupanj studija: diplomski
Akademski / stručni naziv: magistar/magistra inženjer/inženjerka strojarstva (mag. ing. mech.)
Vrsta resursaTekst
Način izrade datotekeIzvorno digitalna
Prava pristupaOtvoreni pristup
Datum isteka embarga: 2022-01-17
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2019-05-24 13:05:35