| Naslov (engleski) | Li2O-WO3-P2O5 glasses - conductivity spectra |
| Autor | Ana Šantić Ruđer Bošković Institute |
| Znanstveno / umjetničko područje, polje i grana | PRIRODNE ZNANOSTI Kemija Anorganska kemija |
| Sažetak (engleski) | Conductivity spectra of 40Li2O–xWO3–(60−x)P2O5, x = 0, 10, 20, 30, 40, 50 mol%, glasses were measured in a frequency range from 0.01 Hz to 1 MHz and temperature range from –90 °C to 240 °C using the impedance analyzer (Novocontrol Alpha-AN Dielectric Spectrometer, Novocontrol Technologies GmbH & Co. KG, Montabaur, Germany). The temperature was controlled to an accuracy of ±0.2 °C. |
| Metodologija (engleski) | Impedance spectroscopy measured in a wide frequency (0.01 Hz to 1 MHz) and temperature (–90 °C to 240 °C) range. Instrumentation: Novocontrol Alpha-AN Dielectric Spectrometer, Novocontrol Technologies |
| Ključne riječi (engleski) | |
| Jezik | engleski |
| URN:NBN | urn:nbn:hr:241:887639 |
| Datum objave | 2024-12-07 |
| Verzija | 1_Li2O-WO3-P2O5 glasses |
| Geolokacija | Zagreb / Bijenička cesta 54, Hrvatska |
| Projekt | Šifra: IP-2018-01-5425 Naziv (hrvatski): Detaljan uvid u mehanizme polaronske i ionske vodljivosti u oksidnoj staklo-(keramici) Naziv (engleski): Expanding insights into the mechanisms of polaronic and ionic conduction in oxide glass-(ceramics) Kratica: POLAR-ION-GLASS Voditelj: Ana Šantić Pravna nadležnost: Hrvatska Financijer: Hrvatska zaklada za znanost Linija financiranja: Istraživački projekt |
| Izdavač | Institut Ruđer Bošković Ruđer Bošković Institute |
| Prava pristupa | Otvoreni pristup |
| Uvjeti korištenja |  |
| Datum i vrijeme pohrane | 2024-12-07 17:57:52 |