Naslov Utjecaj legirnih elemenata na koroziju bakra : diplomski rad
Naslov (engleski) The influence of alloying elements on the copper corrosion : diploma thesis
Autor Ana Radeljić
Mentor Senka Gudić (mentor) MBZ: 181062
Član povjerenstva Ladislav Vrsalović (predsjednik povjerenstva)
Član povjerenstva Vesna Sokol (član povjerenstva)
Član povjerenstva Senka Gudić (član povjerenstva)
Ustanova koja je dodijelila akademski / stručni stupanj Sveučilište u Splitu Kemijsko-tehnološki fakultet (Odsjek za inženjerstvo i tehnologije) Split
Datum i država obrane 2018-10-10, Hrvatska
Znanstveno / umjetničko područje, polje i grana TEHNIČKE ZNANOSTI Kemijsko inženjerstvo
Sažetak Korozijsko ponašanje Cu i različitih legura Cu (Cu-Al, Cu-Al-Ni, Cu-Al-Mn, Cu-Al-Mn-Ni) u 0.5 mol dm -3 NaCl otopini ispitano je praćenjem vremenske promjene potencijala otvorenog strujnog kruga te primjenom potenciodinamičke polarizacije metode i elektrokemijske imperancijske spektroskopije. Oštećenja na površini nastala polarizacijom potvrđena su pretražnim elektronskim mikroskopom, dok je elementarni sastav korozijskih produkata na površini pojedinog uzorka određen EDS analizom. Ustanovljeno je da legirni element nema neki značajniji utjecaj na mehanizam otapanja bakra. Za sve uzorke, anodna reakcija otapanja Cu kontrolirana je difuzijom topljivog CuCl 2 - u masu otopine (što rezultira u anodnom Tafelovom nagibu od 60 mV/dec), dok je katodna reakcija izlučivanje kisika. Korozijska otpornost ispitivanih uzoraka posljedica je formiranja površinskog sloja čija svojstva prvenstveno ovise o kemijskom sastavu osnovnog metala, tj. o vrsti i sadržaju pojedinih legirnih elemenata u uzorku. Legirni elementi kao što su Al, Ni i Mn utječu pozitivno na pasivaciju bakra, te su svojstva površinskog filma bolja (veći otpor i debljina, kompaktnija struktura). Ustanovljeno je da korozijska otpornost ispitivanih uzoraka raste redom: Cu Cu-Al Cu-Al-Ni Cu-Al-Mn Cu- Al-Mn-Ni. Naime, istim redom smanjuje se korozijska struja, a povećava polarizacijski otpor te kompaktnost i debljina površinskog sloja. SEM i EDS analiza ukazala je na ravnomjerno otapanje čistog Cu, dok je na ispitivanim legurama ustanovljeno prisustvo površinskog oksidnog sloja koji se sastoji od smjese odgovarajućih legirnih elementa.
Sažetak (engleski) The corrosion behavior of Cu and various Cu alloys (Cu-Al, Cu-Al-Ni, Cu-Al-Mn, Cu-Al-Mn-Ni) in 0.5 mol dm -3 NaCl solution was investigated using open circuit potential measurements, potentiodynamic polarization and electrochemical impedance spectroscopy methods. The polarization surface damages were verified by scanning electron microscopy, while the elemental composition of corrosion products on the surface of each sample was determined by EDS analysis. It has been found that the alloying element has no significant influence on the copper dissolution mechanism. For all samples, the anodic reaction of Cu dissolution is controlled by the diffusion of soluble CuCl 2 - species from the electrode surface into bulk solution (which results in an apparent anodic Tafel slope of 60 mV/dec), while the cathode reaction is oxygen evolution. The corrosion resistance of the tested samples is a consequence of the surface layer formation whose properties primarily depend on the chemical composition of the based metal, i.e. the type and content of the individual alloying elements in the investigated samples. Alloying elements like Al, Ni, Mn facilitates passivation of the copper, and improve surface film properties (higher resistance and thickness, more compact structure). It has been found that the corrosion resistance of the tested samples growing in the order: Cu Cu-Al Cu-Al-Ni Cu-Al-Mn Cu-Al-Mn-Ni. Namely, the corrosion current decreases in same order, while the polarization resistance and the compactness and thickness of the surface layer increase. SEM and EDS analysis showed a uniform dissolution of pure Cu while the presence of a surface oxide layer consisting of a mixture of corresponding alloying elements was found on the tested alloys.
Ključne riječi
bakar
korozija bakra
legure s prisjetljivosti oblika
legure bakra
elektrokemijske metode
SEM/EDS analiza
Ključne riječi (engleski)
copper
copper corrosion
shape memory alloy
copper alloys
electrochemical metods
SEM/EDS analysis
Jezik hrvatski
URN:NBN urn:nbn:hr:167:055570
Projekt Šifra: 3405 Naziv: Dizajniranje mikrostrukture funkcionalnih svojstava legura s prisjetljivosti oblika na bazi bakra Kratica: DMFP-CuSMA Voditelj: Mirko Gojić Pravna nadležnost: Hrvatska Financijer: HRZZ
Studijski program Naziv: Kemijska tehnologija; smjerovi: Materijali, Zaštita okoliša, Mediteranske kulture Smjer: Materijali Vrsta studija: sveučilišni Stupanj studija: diplomski Akademski / stručni naziv: magistar/magistra inženjer/inženjerka kemijskog inženjerstva (mag.ing.cheming.)
Vrsta resursa Tekst
Način izrade datoteke Izvorno digitalna
Prava pristupa Otvoreni pristup
Uvjeti korištenja
Javna napomena Ključne riječi doradio knjižničar/ Key words are revised by the librarian
Datum i vrijeme pohrane 2019-01-30 10:00:55