prikaz prve stranice dokumenta Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature
  Preuzmi
PDF 278.46 KB
Znanstveni rad - Izvorni znanstveni rad
Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature
Fizika A, 10 (2001), 4; 191-202. urn:nbn:hr:217:642259
Skoko, Željko; Popović, Stanko

Institucijski repozitorij: Repozitorij Prirodoslovno-matematičkog fakulteta

Citirajte ovaj rad

Skoko, Ž. i Popović, S. (2001). Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature. Fizika A, 10. (4), 191-202. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:217:642259

Skoko, Željko i Stanko Popović. "Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature." Fizika A, vol. 10, br. 4, 2001, str. 191-202. https://urn.nsk.hr/urn:nbn:hr:217:642259

Skoko, Željko i Stanko Popović. "Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature." Fizika A 10, br. 4 (2001): 191-202. https://urn.nsk.hr/urn:nbn:hr:217:642259

Skoko, Ž. i Popović, S. (2001) 'Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature', Fizika A, 10(4), str. 191-202. Preuzeto s: https://urn.nsk.hr/urn:nbn:hr:217:642259 (Datum pristupa: 22.11.2024.)

Skoko Ž, Popović S. Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature. Fizika A [Internet]. 2001. [pristupljeno 22.11.2024.];10(4):191-202. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:217:642259

Ž. Skoko i S. Popović, "Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature", Fizika A, vol. 10, br. 4, str. 191-202, 2001. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:217:642259. [Citirano: 22.11.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:217:642259
Podaci o radu
Naslov (engleski)Dependence of microstructure of Al-44 at% and Al-48 at% zn alloys on temperature
AutorŽeljko Skoko
AutorStanko Popović
Autorova ustanovaSveučilište u Zagrebu
Prirodoslovno-matematički fakultet
(Fizički odsjek)
Znanstveno / umjetničko
područje, polje i grana		PRIRODNE ZNANOSTI
Fizika
Sažetak (engleski)
The temperature dependence of microstructure of the title alloys was studied in situ by XRD. Each alloy had been subjected to two different thermal treatments: (i) rapid quenching from the solid-solution temperature, T_SS, in water at room temperature (RT) and ageing at RT (samples WQ) and (ii) cooling slowly from TSS to RT and ageing at RT (samples SC). As the samples SC were closer to the equilibrium state than the samples WQ, the microstructure of the two sets of samples dependeded on temperature in a different way. The solid solution, aSS, was formed at about 720 K for the samples SC, and at about 880 K for the samples WQ. During the slow cooling to RT the samples SC and WQ behaved in a similar way. Instead of the phase transitions expected according to the phase diagram, the following sequence of transitions was observed for both alloys: α(M/β)+β(Zn) - α¢+β(Zn)+a(M/α¢,β) - α_SS. A similar thermal behaviour was also found for the Zn-rich alloys, Al-54 at% Zn and Al-62 at% Zn.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaFizika A
Brojčani podacivol. 10, br. 4, str. 191-202
p-ISSN1330-0008
URN:NBNurn:nbn:hr:217:642259
Datum objave publikacije2001
URL dokumentahttp://fizika.hfd.hr/fizika_a/av01/a10p191.htm
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2019-10-11 14:52:24