Chemical resistance of cement paste to the action of deionized water
Zagreb: Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet, 2019. urn:nbn:hr:217:449477
Đuroković, Marija
Sveučilište u Zagrebu
Prirodoslovno-matematički fakultet
Kemijski odsjek

Institucijski repozitorij: Repozitorij Prirodoslovno-matematičkog fakulteta

Citirajte ovaj rad

Đuroković, M. (2019). Chemical resistance of cement paste to the action of deionized water (Disertacija). Zagreb: Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:217:449477

Đuroković, Marija. "Chemical resistance of cement paste to the action of deionized water." Disertacija, Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet, 2019. https://urn.nsk.hr/urn:nbn:hr:217:449477

Đuroković, Marija. "Chemical resistance of cement paste to the action of deionized water." Disertacija, Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet, 2019. https://urn.nsk.hr/urn:nbn:hr:217:449477

Đuroković, M. (2019). 'Chemical resistance of cement paste to the action of deionized water', Disertacija, Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet, citirano: 31.12.2024., https://urn.nsk.hr/urn:nbn:hr:217:449477

Đuroković M. Chemical resistance of cement paste to the action of deionized water [Disertacija]. Zagreb: Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet; 2019 [pristupljeno 31.12.2024.] Dostupno na: https://urn.nsk.hr/urn:nbn:hr:217:449477

M. Đuroković, "Chemical resistance of cement paste to the action of deionized water", Disertacija, Sveučilište u Zagrebu, Prirodoslovno-matematički fakultet, Zagreb, 2019. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:217:449477

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:217:449477
Podaci o radu
NaslovChemical resistance of cement paste to the action of deionized water
Naslov (hrvatski)Kemijska otpornost cementne paste prema djelovanju deionizirane vode
AutorMarija Đuroković
MentorDubravka Matković-Čalogović (mentor)
MentorIvan janotka https://orcid.org/0000-0002-3601-5277 (komentor)
Član povjerenstvaSanda Rončević (predsjednik povjerenstva)
Član povjerenstvaDubravka Matković-Čalogović (član povjerenstva)
Član povjerenstvaJelena Bleiziffer (član povjerenstva)
Ustanova koja je dodijelila
akademski / stručni stupanj		Sveučilište u Zagrebu
Prirodoslovno-matematički fakultet
(Kemijski odsjek)
Zagreb
Datum i država obrane2019-12-19, Hrvatska
Znanstveno / umjetničko
područje, polje i grana		PRIRODNE ZNANOSTI
Kemija
Univerzalna decimalna klasifikacija
(UDC)		54 - Kemija. Kristalografija. Mineralogija
Sažetak
Introduction of new, sustainable materials into the existing civil engineering standards requires durability data for different degradation processes. Unfortunately, durability tests are not standardized. In this work degradation process of decalcification, also called leaching, of cement pastes was studied. The research was conducted on three different immature cement pastes. Two Portland cements based on calcium silicate or aluminate compounds and a cement based on calcium sulfoaluminate compounds were used for preparation of cement pastes. The change in chemical composition of cement pastes and pore solutions, phase compositions, microstructures of cement pastes and their mechanical properties (strength, modulus of elasticity, dimensional and mass stability) were observed during a 365 days leaching period. The results indicate no significant impact of leaching on microstructure, modulus of elasticity, dimensional and mass stability. The observed strength decrease correlates with the observed changes in phase and chemical composition of the cement pastes and pore solutions.
Sažetak (hrvatski)
Uvođenje novih materijala u postojeće građevinske norme zahtijeva podatke o trajnosnim svojstvima novih materijala. Nažalost, ispitivanja trajnosnih svojstava materijala nisu standardizirana. U ovom radu je opisano istraživanje procesa degradacije dekalcifikacijom ili izluživanjem. Istraživanje je provedeno na tri različite nezrele cementne paste. Dva tipa portlandskog cementa izgrađenih od kalcijevih silikata ili aluminata i cement izgrađenog od kalcijevih sulfoaluminata korišteni su za izradu uzoraka cementnih pasti u ovom istraživanju. Praćene su promjene kemijskog sastava cementnih pasta i pornih otopina, faznog sastava, mikrostrukture cementne paste kao i mehaničkih svojstava (čvrstoće, modula elastičnosti, promjene dimenzija i mase) u periodu izluživanja od 365 dana. Rezultati ispitivanja ne pokazuju značajan utjecaj izluživanja na mikrostrukturu, modul elastičnosti, dimenzionalnu i masenu stabilnosti. Uočeni pad čvrstoće povezan je s učenim promjenama faznog i kemijskog sastava cementnih pasti i pornih otopina.
Ključne riječi
Ključne riječi (hrvatski)
Jezikengleski
URN:NBNurn:nbn:hr:217:449477
Studijski programNaziv: Kemija
Vrsta studija: sveučilišni
Stupanj studija: poslijediplomski doktorski
Akademski / stručni naziv: doktor/doktorica znanosti, područje prirodnih znanosti, polje kemija (dr. sc.)
Vrsta resursaTekst
Opseg160 str. ; 30 cm
Način izrade datotekeIzvorno digitalna
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2020-01-27 13:18:22