The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors
Materials, 17 (2024), 3; 1-12. https://doi.org/10.3390/ma17030710
Rodinger, Tomislav; Ćorić, Danko; Kováčik, Jaroslav

Institucijski repozitorij: Repozitorij Fakulteta strojarstva i brodogradnje Sveučilišta u Zagrebu

Citirajte ovaj rad

Rodinger, T., Ćorić, D. i Kováčik, J. (2024). The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors. Materials, 17. (3), 1-12. doi: 10.3390/ma17030710

Rodinger, Tomislav, et al. "The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors." Materials, vol. 17, br. 3, 2024, str. 1-12. https://doi.org/10.3390/ma17030710

Rodinger, Tomislav, Danko Ćorić i Jaroslav Kováčik. "The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors." Materials 17, br. 3 (2024): 1-12. https://doi.org/10.3390/ma17030710

Rodinger, T., Ćorić, D. i Kováčik, J. (2024) 'The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors', Materials, 17(3), str. 1-12. doi: 10.3390/ma17030710

Rodinger T, Ćorić D, Kováčik J. The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors. Materials [Internet]. 01.02.2024. [pristupljeno 27.06.2024.];17(3):1-12. doi: 10.3390/ma17030710

T. Rodinger, D. Ćorić i J. Kováčik, "The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors", Materials, vol. 17, br. 3, str. 1-12, Veljača 2024. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:235:512312. [Citirano: 27.06.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:235:512312
Podaci o radu
Naslov (engleski)The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors
AutorTomislav Rodinger
AutorDanko Ćorić
AutorJaroslav Kováčik
Autorova ustanovaSveučilište u Zagrebu
Fakultet strojarstva i brodogradnje
(Zavod za materijale)
(Katedra za materijale i tribologiju)
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Strojarstvo
Proizvodno strojarstvo
Sažetak (engleski)
Various foaming agents can be used to achieve foaming of the precursors obtained by using the powder metallurgy method. However, the thermal behavior of pure aluminum precursors with different foaming agents has been studied very little in recent times. For the production of aluminum foams with closed cells, 1 wt.% of calcium carbonate (CaCO3), titanium hydride (TiH2), heat-treated TiH2 and zirconium hydride (ZrH2) were used. The foaming capability of the compacted precursors was investigated at temperatures 700, 720 and 750 °C. CaCO3 and TiH2 showed the best foamability at all considered temperatures, while ZrH2 achieved relatively good foaming only at the highest temperature, 750 °C. Due to their low onset temperature of the decomposition compared to the melting point of the unalloyed aluminum, in hydride-based foaming agents the drainage occurred at the bottom part of the foam samples. Among the investigated foaming agents, precursors with heat-treated TiH2 had the worst foaming properties, while CaCO3 showed the best foamability without the occurrence of drainage.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran - međunarodna recenzija
Verzija publikacijeZavršna verzija rukopisa prihvaćena za objavljivanje (postprint)
Naslov časopisaMaterials
Brojčani podacivol. 17, br. 3, str. 1-12, 710
e-ISSN1996-1944
DOIhttps://doi.org/10.3390/ma17030710
URN:NBNurn:nbn:hr:235:512312
Datum objave publikacije2024-02-01
URL dokumentahttps://www.mdpi.com/1996-1944/17/3/710
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Imenovanje 4.0 međunarodna (CC BY 4.0)
Datum i vrijeme pohrane2024-05-22 11:08:30